These issues mainly depend on the content of calcium carbonate powder (commonly known as lime powder) in the edge banding strip. Generally, PVC edge banding contains calcium carbonate powder, but excessive content of calcium carbonate powder can cause the structure of PVC to become loose, thereby seriously affecting the quality of PVC edge banding. The problems caused by the high content of calcium carbonate powder include:Folding white refers to the phenomenon of whitening at the bent edge afte

Many people think that to solve the problem of color inconsistency in PVC edge banding processing, as long as the yellowing profile production line to reduce the processing temperature, can reduce the color difference. But it is also believed that yellowing is the impact of PVC, CPE, stabilizer, different batches of PVC, CPE, stabilizer and other main auxiliary raw materials, processing there will be different color. In this case, even if the single addition of a certain amount of whitening agen

The use of furniture is relatively long, but you have not found that some families with furniture for many years without any signs of bad, or even new as just bought back. On the contrary, their furniture, not a few years to produce some cracks, de-lacquer and other aspects of the problem. In fact, the durability of furniture is related to daily maintenance. Small series summed up three don’t, four forbidden and four as far as possible furniture maintenance skills, let your furniture use a few

The commonly used edge banding in furniture has many functions, such as moisture-proof, anti-corrosion, furniture protection, etc., but few people really pay attention to this aspect. With the changing consumer attitudes towards furniture, edge sealing functions such as environmental protection, aesthetics, durability, and environmental friendliness will become the focus of attention for end consumers. Next, let's invite the edge banding manufacturer to introduce the main functions of edge b

1, PVC edge of the bad phenomenon of plasticizing(1)the surface of plastic layer has the phenomenon of toad skin. (2)the temperature control is low, the instrument pointer reflects the low temperature, the actual measuring temperature is also low. (3)the surface of plastic is black, and there are small cracks or small particles without plasticization. (4)the plastic plywood stitches badly, there is an obvious trace.2. The reasons of bad plasticization of PVC edge-sealing strip(1) the temperature

For different materials of the edge of what is different, through learning and observation, found that it is easy to distinguish should be the use of combustion, here to tell you the summary of the results.PVC sealing strip (PVC) is difficult to fire, burning yellow and green smoke, there is a pungent smellPP edge banding (pp) is easy to catch fire, there is a smell of oilABS (acrylonitrile-butadiene-styrene copolymer) slow combustion, special smellAcrylic material is easy to melt and blister, t